CPCt1-FS Transparent Front Plate price_Manufacturer_How much

1/1

CPCt1-FS Transparent Front Plate

Negotiable

Lucky Film Company Limited

Located Region:

China

Address:

No. 6, Lekai South Street, Jingxiu District, Baoding City, Hebei Province

Biz Consulting:

+86 3128943797

WhatsApp:

+8618531282120

E-mail:

zhaosf@lkintl.com

Online Contact

Favorite

The independently developed UV-resistant lifting technology, anti-reflective technology, and coating hardness enhancement technology give the transparent front plate high weather resistance, high light transmittance, and high scratch resistance. It meets the lightweight requirements of modules and can be widely applied to distributed projects such as low-load rooftops and building curtain walls.

Product Features:

Excellent UV resistance: UV resistance > 1000 kWh/m², high retention of elongation at break.
High light transmittance: Light transmittance ≥ 90%.
High scratch resistance: High hardness and high strength.

Serial Number	Project		Unit	Technical specifications	Inspection method
1	Thickness		μm	305 _-5⁺¹⁵	GB/T 13542.2-2009
2	Tensile Strength (MD/TD)		MPa	≥ 100/100	GB/T 13542.2-2009
3	Elongation at break (MD/TD)		%	≥ 100/100	GB/T 13542.2-2009
4	Adhesion		Level	0	GB/T 9286-1998
5	Dimensional stability (MD/TD)		%	≤ 1.0/0.5	GB/T 13542.2-2009
6	Peel strength with EVA		N/cm	≥ 40	GB/T 2790-1995
7	Breakdown voltage		kV	≥ 18	GB/T 13542.2-2009
8	Light transmittance (400-1100nm)		%	≥ 85	GB/T 2410-2008
9	UV blocking rate (280-380nm)		%	≥ 95	GB/T 2410-2008
10	Water vapor transmission rate		g/m² ·d	≤ 2.0	GB/T 26253-2010
11	Volume resistivity		Ω ·m	≥ 1 × 10¹³	GB/T 1410-2006
12	Moisture-heat aging (85 ℃ 85%RH)1000h	Adhesion	Level	0	GB/T 9286-1998
		Tensile strength retention (MD/TD)	%	≥ 80/80	GB/T 13542.2-2009
		Retention rate of elongation at break (MD/TD)	%	≥ 60/60	GB/T 13542.2-2009
		Peel strength with EVA	N/cm	≥ 30	GB/T 2790-1995
		Yellowing	△b	≤ 3.0	GB/T 7975-2005
		Transmittance retention rate	%	≥ 95	GB/T 2410-2008
		Apparent	-	No delamination, no blistering	-
13	UV aging 1000kWh/m²	Adhesion	Level	0	GB/T 9286-1998
		Tensile strength retention (MD/TD)	%	≥ 30/30	GB/T 13542.2-2009
		Elongation at break retention rate/ (MD/TD)	%	≥ 30/30	GB/T 13542.2-2009
		Yellowing	△b	≤ 3.0	GB/T 7975-2005
		Transmittance retention rate	%	≥ 95	GB/T 2410-2008
		Apparent	-	No delamination, no blistering	-